Internal friction study on the mobility of screw dislocations in undoped InSb

Abstract
Dislocation mobility is studied by low frequency internal friction in undoped InSb between 0.1 and 0.98 Tm. Samples characterized by a mainly screw dislocations substructure generated by low temperature (403 K) deformation, reveal two high amplitude peaks located at 570 and 725 K. The 570 K-peak symmetrically shaped is explained as an intrinsic relaxation peak of screw dislocations moving by double kink nucleation followed by their lateral propagation. The peak analysis leads to an activation energy 1.27 ± 0.11 eV, close to the apparent activation energy of the InSb plastic deformation.

Résumé
La mobilité des dislocations a été étudiée dans InSb non dopé par frottement intérieur basse fréquence (1 Hz) entre 0,1 et 0,98 Tm. Avec une sous-structure composée essentiellement de dislocations vis engendrée par déformation plastique à 403 K, on a mis en évidence deux pics d'amplitude importante situés à 570 K et 725 K. Le pic à 570 K, d'allure symétrique, est interprété comme un pic de relaxation intrinsèque de dislocations vis par nucléation de doubles décrochements, suivie de la propagation latérale de chaque décrochement. L'analyse de ce pic conduit à une énergie d'activation de 1,27 ± 0,11 eV voisine de celle de la déformation plastique.