Rev. Phys. Appl. (Paris) 24, 479-483 (1989)
DOI: 10.1051/rphysap:01989002405047900
Supraconductivité en dessous de 120 K de nouveaux composés au thallium
B. Giordanengo1, 2, M. Hervieu3, A. Maignan3, C. Martin3, C. Michel3, J. Provost3, B. Raveau3, A. Sulpice1 et R. Tournier11 CRTBT, CNRS B.P. 166X, 38042 Grenoble, France
2 MERLIN-GERIN, Usine A 2 rue H. Tarze, 38000 Grenoble, France
3 CRISMAT, Bd Maréchal Juin, 14032 Caen, France
Abstract
Well-cristallized Tl2Ba2CaCu2O8 phases have been observed superconducting or normal below 108 K depending on their stoichiometry. This observation is an evidence that a (CuII -O-) mixed valence induced by vacancies or substitutions on different sites gives rise to superconductivity in this phase. The new phase TlBa2Ca2Cu3O9 which intrinsically contains a mixed valence has been observed as having a sharp transition to bulk superconductivity in the Meissner effect at a critical temperature of 120 K.
Résumé
Des échantillons de la phase Tl2Ba2CaCu2O8 bien cristallisée ont été observés supraconducteurs ou normaux en dessous de 108 K suivant leur stoechiométrie. Cette observation montre que la valence mixte (CuII-O-) induite par les lacunes ou les substitutions sur les différents sites accroît la supraconductivité de cette phase. La nouvelle phase TlBa2Ca2Cu3O9, qui contient intrinsèquement une valence mixte, a été observée, en effet Meissner, supraconductrice en volume avec une transition étroite à 120 K.
7410 - Superconducting critical temperature, occurrence.
7470V - Perovskite phase superconductors.
7430C - Magnetic properties of superconductors.
Key words
barium compounds -- calcium compounds -- high temperature superconductors -- Meissner effect -- mixed valence compounds -- stoichiometry -- superconducting transition temperature -- thallium compounds -- mixed valence -- 120 K -- Tl sub 2 Ba sub 2 CaCu sub 2 O sub 8 -- TlBa sub 2 Ca sub 2 Cu sub 3 O sub 9