Rev. Phys. Appl. (Paris) 9, 673-681 (1974)
DOI: 10.1051/rphysap:0197400904067300

Comptage de stries sur alliages légers rompus en fatigue

J. Odorico et Ph. Le Gall

S. N. I. A. S. 12, rue Pasteur, 92150 Suresnes, France

Abstract
Experimental measurement of fatigue striation spacing on centrally notched fracture surface of AU4G1-T 3 specimens, 2 mm thick, AU4G1-T 351, 1.5 mm thick, AU2GN-T 651, 1.5, 3 and 5 mm thick have been realized. We have found some correlation between the macroscopic crack growth rate and the average value of striation spacing. This correlation depends slightly on the thickness and are available for crack growth rate da/dN from 0.05 μ/cycle to 0.5 μ/cycle. From these results we can obtain the relation between : - the number of striation spacings and the number of load cycles, - the average striation spacing and the imposition of peak loads in the loading sequence.

Résumé
Des comptages systématiques de stries de fatigue des éprouvettes rompues de type IRWIN en A-U4G1 T 3, d'épaisseur e = 2 mm, en A-U4G1 T 351 e = 1,5 mm, en A-U2GN T 651 e = 1,5 mm, e = 3 mm et e = 5 mm nous ont permis de trouver des corrélations entre les vitesses macroscopiques de fissuration et les distances moyennes entre les stries. Ces corrélations dépendent légèrement de l'épaisseur et sont valables pour des vitesses de fissuration da/dN allant de 0,05 μ/cycle à 0,5 μ/cycle. De ces résultats nous pouvons déduire des relations entre : - le nombre de stries et le nombre de cyclage de contrainte, - les distances moyennes entre les stries et la contrainte maxi appliquée pendant la propagation.

PACS
6220M - Fatigue, brittleness, fracture, and cracks.
8130 - Phase diagrams and microstructures developed by solidification and solid solid phase transformations.
8140N - Fatigue, embrittlement, and fracture.

Key words
alloys -- aluminium alloys -- cracks -- fatigue -- fatigue striations -- notched light alloys -- macroscopic crack growth rate