Rev. Phys. Appl. (Paris) 23, 475-478 (1988)
DOI: 10.1051/rphysap:01988002304047500
Institut für Festkörperphysik, Universität Wien, 1090 Boltzmanngasse 5, Vienna, Austria
6172L - Linear defects: dislocations, disclinations.
6172M - Grain and twin boundaries.
Key words
Dislocation motion -- Grain boundaries -- Dislocation glide -- Hardening
DOI: 10.1051/rphysap:01988002304047500
Grain boundaries (moderator's comment)
H.O.K. KirchnerInstitut für Festkörperphysik, Universität Wien, 1090 Boltzmanngasse 5, Vienna, Austria
Abstract
Grain boundaries are an effective obstacle to dislocation motion. The resulting incompatibility stress causes multiple slip. Adjacent to the grain boundary the crystal is in an advanced stage of hardening. Transgranular slip is quantitatively unimportant.
Résumé
Les joints de grains sont des obstacles effectifs pour le mouvement des dislocations. Les contraintes d'incompatibilité associée causent du glissement multiple. Dans la vicinité du joint le cristal se trouve dans un état avancé du durcissement. Le cisaillement transgranulaire est quantitativement peu important.