Analyse micromécanique de la rupture des composites céramiques

P. Pérès, L. Anquez et J. Jamet

ONERA, B.P. 72, 92322 Châtillon-sous-Bagneux, France

Abstract
The fracture mechanic analysis of a basic ceramic-ceramic composite (filament + coating) is based on two main assumptions : local adaptation by sliding between fibre and matrix when a crack in the matrix appears, and statistical distribution of defects. The consequences of such assumptions concerning the multicracking of the matrix explain the non linear behaviour of such composites. They are discussed in relation with experimental results obtained on unidirectional multifilaments SiC/alumina composites.

Résumé
L'analyse mécanique du comportement à la rupture d'un composite céramique/céramique élémentaire constitué d'une fibre gainée de matrice s'appuie sur deux hypothèses essentielles : d'une part l'adaptation locale par glissement fibre-matrice à l'apparition d'une fissure matricielle, et d'autre part la distribution statistique de défauts. Les conséquences de ces hypothèses sur la multifissuration matricielle, sur les comportements non linéaires des composites monofilamentaires sont discutées au regard des résultats expérimentaux sur composites unidirectionnels multifilamentaires SiC/alumine.

PACS
6220M - Fatigue, brittleness, fracture, and cracks.
8140N - Fatigue, embrittlement, and fracture.

Key words
alumina -- ceramics -- composite materials -- fracture -- silicon compounds -- ceramic composites rupture -- fracture mechanic analysis -- statistical distribution -- defects -- multicracking -- SiC fibre reinforced Al sub 2 O sub 3