Influence de l'environnement sur la propagation des fissures courtes et longues dans un alliage léger type 7075

A. Zeghloul et J. Petit

Laboratoire de Mécanique et Physique des Matériaux, URA CNRS 863, E.N.S.M.A., 86034 Poitiers Cedex, France

Abstract
The growth in fatigue of small bidimensionnal cracks has been studied in air and in vacuum on the 7075 T651 Aluminum alloy (peak aged) and in air at two load ratio, on the 7075 T7351 alloy (overaged). The low growth rate range was investigated near threshold conditions. On the basis of crack closure measurements and long cracks propagation results, it was shown that, for given environmental conditions, the behaviour of small and long cracks can be described in terms of the effective stress intensity factor range.

Résumé
La propagation en fatigue des fissures courtes bidimensionnelles a été étudiée à l'air et dans le vide dans l'alliage 7075 T651 (vieilli au pic de durcissement) et à l'air pour deux rapports de charge dans l'alliage 7075 T7351 (sur-revenu). Les essais ont été effectués dans le domaine des basses vitesses de fissuration au voisinage du seuil de non-propagation. Sur la base des mesures de fermeture de fissure et des résultats relatifs à la propagation des fissures longues, il est montré que, pour un environnement donné, la propagation des fissures de petites dimensions peut être décrite à l'aide d'une seule relation liant la vitesse de fissuration au facteur d'intensité de contrainte effectif ΔKeff.

PACS
8140N - Fatigue, embrittlement, and fracture.
6220M - Fatigue, brittleness, fracture, and cracks.

Key words
aluminium alloys -- crack edge stress field analysis -- fatigue cracks -- aging -- environment -- fatigue -- cracks -- air -- vacuum -- 7075 T651 -- effective stress intensity factor -- Al alloy