Élaboration et transformation d'alliages binaires à base de niobium à l'état de grande pureté

R. Geschier1, A. Clauss1, H. Forestier1, J.P. Givord2 et M. Armand2

1  Département Sciences de Matériaux, E. N. S. C., Strasbourg, 1, rue Blaise-Pascal, 67, Strasbourg
2  Laboratoire de Recherches de Venthon, Sté Ugine-Kuhlmann, 73, Albertville


Abstract
This paper concerns the preparation and the transformation of Nb-rich alloys made by melting high purity metals. Nb-Zr and Nb-Mo alloys have been prepared by electronbeam melting ; Nb-Ti alloy has been prepared by vacuum-arc melting. After cold-forging of the cast ingots, the alloys have been either cold-rolled until 1 mm thick, or cold-swaged until 0,3 mm diameter. Experimental conditions are precised.


Résumé
A partir de métaux très purs les alliages binaires suivants ont été élaborés par fusion par bombardement électroniques : Nb-Zr à 2,0, 3,85, 5,45 % at Zr et Nb-Mo à 5,3 % at Mo. Un alliage Nb-Ti à 4,65 % at Ti a été préparé au four à arc. Ces alliages, sous forme de lingots de 4 kg environ, présentent une bonne homogénéité. Leur pureté est supérieure à 99,97 %. Après forgeage en plats, ces alliages sont transformés à froid, soit par laminage jusqu'à 1 mm, soit par retreinte à l'état de fils jusqu'à 0,3 mm de diamètre. Les conditions opératoires sont précisées et on rend compte des difficultés rencontrées et de l'expérience acquise.

PACS
8120G - Preparation of metals and alloys compacts, pseudoalloys.
8140 - Treatment of materials and its effects on microstructures and properties.