Microhardness of aged NiO single crystal

J. Cabrera-Cano, A. Dominguez-Rodriguez, R. Marquez et J. Castaing

Departamento de Optica de la Facultad de Ciencias de la Universidad de Sevilla, Spain


Abstract
The effects of ageing on the plastic properties of NiO single crystals were determined in samples doped with 20 ppM to 2 500 ppM manganese. Microhardness and slip band length were measured. Maximum microhardness occurs for very short ageing time at 550 °C and 850 °C ; on the contrary, slip band length shows no minimum and shows strengthening only after ageing at 550 °C. These effects can be attributed to various aggregation states of point defects.


Résumé
On a étudié l'effet du vieillissement sur les propriétés plastiques de monocristaux de NiO dopés avec 20 à 2 500 ppM de manganèse à l'aide de mesures de microdureté et de longueur de bande de glissement. Un maximum de microdureté apparait après des temps très courts de vieillissement à 550 °C et 850 °C ; par contre, les longueurs de bande de glissement ne passent pas par un minimum et indiquent un durcissement seulement à 550 °C. Ces résultats peuvent être attribués à divers états d'agrégation des défauts ponctuels.

PACS
6170L - Slip, creep, internal friction and other indirect evidence of dislocations.
6220F - Deformation and plasticity.
6220M - Fatigue, brittleness, fracture, and cracks.
8140G - Other heat and thermomechanical treatments.
8140L - Deformation, plasticity and creep.
8140N - Fatigue, embrittlement, and fracture.

Key words
ageing -- hardness -- manganese -- nickel compounds -- plasticity -- slip -- aged NiO single crystal -- plastic properties -- slip band length -- microhardness -- NiO:Mn