Laser solide à fonctionnement continu à la température ambiante

Abstract
A method of synthesis of neodymium doped calcium tungstate single crystals is described (Nd concentration from 0.5 to 2 per cent) : by melting in iridium crucibles, with moist argon circulation, and high frequency heating. Cristals are pulled with α-axis orientation, with a speed of growth of 11,5 mm/hour, and are annealed during 15 hours at 1 300 °C. Rods, cut from these crystals, have shown continuous laser operation at room temperature with an apparatus described here. The thresholds are 420 and 900 watts, the pumping lamp being supplied with a. c. and d. c. respectively. The output power, for one kilowatt input power, is more than half a watt.

Résumé
On décrit une méthode de synthèse des monocristaux de tungstate de calcium dopé au néodyme (concentration : 0,5 à 2 %) : fusion en creuset d'iridium, sous balayage d'argon humide, par chauffage haute fréquence. Les cristaux sont tirés suivant l'axe a, à la vitesse de 11,5 mm/heure. Ils subissent ensuite un recuit de 15 heures à 1 300 °C. Les barreaux découpés dans ces cristaux ont présenté l'effet laser en continu à la température ordinaire, dans une installation dont les principales caractéristiques sont indiquées. Les seuils de fonctionnement sont de 420 watts, et 900 watts, la lampe de pompage étant alimentée en courant alternatif et continu respectivement. La puissance émise, pour une puissance de pompage de 1 kwatt, dépasse 0,5 watt.