Quelques propriétés électrochimiques du niobium
Jacques Pagetti et Jean TalbotLaboratoire de Génie Chimique. Ecole Nationale Supérieure de Chimie de Paris, 11, rue Pierre-et-Marie-Curie, Paris 5e
Abstract
Corrosion of niobium in various acid and alkaline media, at room temperature, has been studied using electrochemical methods. An electrolytic polishing method is developed in order to obtain a well defined reproductible surface. The good resistance of niobium in acidic solutions, except fluorhydric acid, has been attributed to a protective film of niobium oxide. Preliminary results have been obtained on the anodic behaviour of niobium in deaerated sodium hydroxide. In addition, the effect of dissolved oxygen on the corrosion of niobium has been examined.
Résumé
Le comportement du niobium dans les solutions acides et alcalines a été étudié par des méthodes électrochimiques. Afin d'obtenir un état de surface bien défini nous avons mis au point une méthode de polissage électrolytique du niobium. La tenue remarquable du niobium dans les acides à l'exception de l'acide fluorhydrique, peut être attribuée à la formation d'un film d'oxyde protecteur. Dans le milieu alcalin la vitesse de corrosion du métal dépend de la concentration du réactif d'une part et de la teneur en oxygène dissous d'autre part.
8245B - Corrosion and passivation.
Key words
Electrochemical corrosion -- Anodic polarization -- Electropolishing -- Acidic solution -- Basic solution -- Oxide layer -- Corrosion protection -- Corrosion rate -- Niobium -- Experimental study