Une étude expérimentale et théorique du comportement en fluage biaxial de l'aluminium A5 (99,5 % en poids) aux températures intermédiaires (300 °C à 450 °C)

C. Lexcellent et J. Birocheau

Laboratoire de Mécanique Appliquée, Université de Besançon, UFR Sciences et Techniques, route de Gray, La Bouloie, 25030 Besançon Cedex, France

Abstract
For an intermediate range of temperature (300 ≤ T ≤ 450 °C), we performed measurements in steady state creep of the strain hardening parameter hst, the recovery rate rst and the intemal stress Xstij). The dependence of r and h on intemal stress is the same in the stationary state as in the initial state just before beginning creep test (cf. Measurements on A99 Nakashima et al. (1987)). This enables us to extend the results to different temperatures and to transients states of the dissipative pseudo potential Ω(σij, Xij), already identified for steady state.

Résumé
Des mesures en fluage stationnaire du paramètre d'écrouissage h st, de restauration rst et de la contrainte interne Xstij sont effectués aux températures intermédiaires (300 ≤ T ≤ 450 °C). La dépendance de r et h avec la contrainte interne est identique dans l'état stationnaire à celle mesurée aux premiers instants du fluage (cf. mesures sur l'A99 de Nakashima et al., 1987). Cela permet l'extension en température et pour des états transitoires du pseudo-potentiel de dissipation Ω(σij, Xij, T) déjà identifié en stationnaire.

PACS
8140L - Deformation, plasticity and creep.
6220H - Creep.
8140E - Cold working, work hardening: post deformation annealing, recovery and recrystallisation: textures.

Key words
aluminium -- creep -- internal stresses -- work hardening -- biaxial creep -- aluminium A5 -- intermediate temperatures -- strain hardening -- recovery -- internal stress -- transients states -- dissipative pseudopotential -- 300 to 450 degC -- Al