Rev. Phys. Appl. (Paris) 17, 377-381 (1982)
DOI: 10.1051/rphysap:01982001706037700

Origine de la biréfringence naturelle observée dans les cristaux de ZnSe cubique

J. Baillou

Laboratoire d'Optoélectronique, UER Sciences, 40, avenue du Recteur Pineau, 86022 Poitiers, France

Abstract
ZnSe single crystals prepared by the vapour phase technique grow with the zincblende structure. However these crystals exhibit a weak native birefringence due to structural defects. The results of measurements of this phenomenon are related and compared with the results previously published by several authors. Two assumptions are proposed to explain the origin and the dispersion of the birefringence ; it is shown that this later results first from a stress applied along the [110] axis and secondly from spatial dispersion, these both causes can be existing simultaneously.

Résumé
Les monocristaux de ZnSe préparés par condensation de la phase vapeur cristallisent dans le système de la blende. Cependant ils présentent des défauts de structure qui leur confèrent une faible biréfringence naturelle. Les résultats des mesures relatives à ce phénomène sont exposés, et en les comparant avec ceux obtenus par plusieurs auteurs, deux hypothèses sont proposées sur l'origine et la dispersion de la biréfringence : il apparaît que celle-ci est due à un effet de contrainte d'axe [110] et à un effet de dispersion spatiale, ces deux causes possibles ayant lieu simultanément.

PACS
7820F - Birefringence condensed matter.

Key words
birefringence -- II VI semiconductors -- zinc compounds -- vapour phase crystal growth -- axial stress -- II VI semiconductor -- ZnSe single crystals -- weak native birefringence -- structural defects -- [110] axis -- spatial dispersion